Method for producing a cathode steel bar with copper insert, and method for removing a copper insert from a used cathode bar
Application number
20201415
Case type
National
Status
10.02.2025 Patent meddelt (B1)
Filed
21.12.2020
Effective date
21.12.2020
Publicly available
22.06.2022
Next annual fee due
31.12.2026
Applicant
STORVIK AS (NO)
Owner
STORVIK AS (NO)
Inventor
Bjarte Valåmo (NO) et al.
Agent
ZACCO NORWAY AS (NO)
Granted
10.02.2025
Patent number
348485
Expiry date
21.12.2040

Abstract and drawing

Disclaimer: This text has been machine-scanned and may contain errors – please refer to "Publications" for legally binding content.
The present invention relates to a method for producing a cathode steel bar with copper insert for use in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process. The present invention further relates to a method of removing a copper insert from a cathode bar used in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, and reusing the copper from old copper inserts in production of new cathode bars with copper insert.

Publications

Latest published versionB1A1

Documents

 Expand Download files (33)
Date
 Date Doc. No. Process Case number In/Out Journal description To/from
 12.02.2025 13-01 Saksbehandling 20201415(348485) UT PT Registreringsbrev nasjonal patent (15) (PT20201415)
18.11.2024 12-01 Saksbehandling 20201415 UT PT Meddelelse om patent ZACCO NORWAY AS
 14.11.2024 11-02 Saksbehandling 20201415 INN P342103NO00 - Claims of 2024-05-27 ZACCO NORWAY AS
 14.11.2024 11-01 Saksbehandling 20201415 INN Korrespondanse (Hovedbrev inn) ZACCO NORWAY AS
 17.10.2024 10-04 Saksbehandling 20201415 INN Svar på uttalelse ZACCO NORWAY AS
 17.10.2024 10-03 Saksbehandling 20201415 INN Endret beskrivelse (renskrevet) ZACCO NORWAY AS
 17.10.2024 10-02 Saksbehandling 20201415 INN Endret beskrivelse (merket) ZACCO NORWAY AS
 17.10.2024 10-01 Saksbehandling 20201415 INN Korrespondanse (Hovedbrev inn) ZACCO NORWAY AS
 11.10.2024 09-01 Saksbehandling 20201415 UT Realitet patent ZACCO NORWAY AS
 27.05.2024 08-05 Saksbehandling 20201415 INN P342103NO00 - Response to 2nd OA ZACCO NORWAY AS
 27.05.2024 08-04 Saksbehandling 20201415 INN P342103NO00 - NO translation of accepted claims ZACCO NORWAY AS
 27.05.2024 08-03 Saksbehandling 20201415 INN P342103NO00 - Amended description and claims Marked ZACCO NORWAY AS
 27.05.2024 08-02 Saksbehandling 20201415 INN P342103NO00 - Amended description and claims Clean ZACCO NORWAY AS
 27.05.2024 08-01 Saksbehandling 20201415 INN Korrespondanse (Hovedbrev inn) ZACCO NORWAY AS
 04.03.2024 07-01 Saksbehandling 20201415 UT 20201415_1823010_PT 08 ZACCO NORWAY AS
 03.11.2022 06-01 Saksbehandling 20201415 UT PT Varsel om betaling av første årsavgift (3317) (PT20201415)
20.10.2021 05-04 Saksbehandling 20201415 INN P342103NO00_ Amended claims_annotated ZACCO NORWAY AS
 20.10.2021 05-03 Saksbehandling 20201415 INN P342103NO00_ Amended claims ZACCO NORWAY AS
 20.10.2021 05-02 Saksbehandling 20201415 INN P342103NO00 - Response to 1st Office Action ZACCO NORWAY AS
 20.10.2021 05-01 Saksbehandling 20201415 INN Korrespondanse (Hovedbrev inn) ZACCO NORWAY AS
 21.04.2021 04-02 Saksbehandling 20201415 UT PT report 02:43:34
21.04.2021 04-01 Saksbehandling 20201415 UT Realitet patent ZACCO NORWAY AS
 28.12.2020 03-01 Saksbehandling 20201415 UT Infobrev til oppfinner ZACCO NORWAY AS
 22.12.2020 02-03 Saksbehandling 20201415 INN P62002233NO00 Online receipt ZACCO NORWAY AS
 22.12.2020 02-02 Saksbehandling 20201415 INN P62002233NO00 Online form ZACCO NORWAY AS
 22.12.2020 02-01 Saksbehandling 20201415 INN Korrespondanse (Hovedbrev inn) ZACCO NORWAY AS
 21.12.2020 01-07 Saksbehandling 20201415 INN P62002233NO00_Specification ZACCO NORWAY AS
 21.12.2020 01-06 Saksbehandling 20201415 INN P62002233NO00_Figures 1-9 ZACCO NORWAY AS
 21.12.2020 01-05 Saksbehandling 20201415 INN P62002233NO00_Claims ZACCO NORWAY AS
 21.12.2020 01-04 Saksbehandling 20201415 INN P62002233NO00_Abstract ZACCO NORWAY AS
 21.12.2020 01-03 Saksbehandling 20201415 INN P62002233NO00 Executed declaration ZACCO NORWAY AS
 21.12.2020 01-02 Saksbehandling 20201415 INN Generalfullmakt_Storvik AS ZACCO NORWAY AS
 21.12.2020 01-01 Saksbehandling 20201415 INN Søknadsskjema Patent ZACCO NORWAY AS

Description, claims and drawings

Disclaimer: This text has been machine-scanned and may contain errors – please refer to "Publications" for legally binding content. Description
Technical fieldThe invention relates to the technical field of electrolysis in molten salts for making aluminium using the Hall-Héroult process. More precisely, the present invention relates to improved cathode steel bars with copper insert, a method for producing such cathode steel bars possibly from used cathode steel bars, and a method for removing copper inserts from used cathode steel bars.Background artAluminium is commonly produced by electrolysis of alumina (aluminium oxide) dissolved in a molten cryolite bath. A Hall-Héroult type electrolytic cell for such production comprises a steel shell (pot shell) with a lining of refractory material, where the bottom of the cell is a carbon cathode having several current collectors embedded therein, and several anode blocks that are partly submerged in the electrolyte bath, and arranged at a distance above the cathode. In industrial production of aluminium the cells of the Hall-Héroult type are connected electrically in series, and the solution of alumina in molten cryolite is brought to a temperature up to about 980 °C by the heating effect of the current traversing through the cell. The thus formed aluminium metal accumulates in the cell bottom, on the cathode surface, and is regularly tapped from the cell.In more detail, the cathode consists of a carbon liner with several cathode steel bars to conduct electric current out of the cell. The cathode steel often has copper inserts at least along parts of the length of the cathode steel, in order to improve the distribution of current along the cathode, see e.g. NO 343609, WO 01/63014, WO 01/27353, CN 210237797.The lifetime of a cathode in an electrolysis cell may be a few years before relining of the cell is needed. Used cathode steel with copper inserts usually has a low value for recycling, and must be replaced by new ones in a lined cell.There are various ways to produce cathode steel with a copper insert. One method is to drill a longitudinal hole in the steel bar with a diameter corresponding to a copper rod to be inserted. The steel bar is heated and crimped around the copper rod. This method requires high precision as the clearance between the hole in the steel and the copper rod must be small, approx.0.5 mm, to ensure sufficiently good contact between the steel and the copper insert. The said method also has limitations in terms of the design of the cross section of the copper insert.Therefore, there is a desire for an improved method of producing cathode steel bars with copper insert of good quality. Thus, it is an objective of the present invention to mitigate, alleviate or eliminate one or more of the disadvantages of today’s solutions in this technical field.Summary of inventionThe invention is set out in the appended set of claims.In a first aspect, the present invention relates to a method of producing a cathode steel bar with copper insert for use in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, comprising:i) providing a steel portion of the cathode steel bar equipped with a cavity for the copper insert and a sleeve on the upper part,providing one or more solid copper item(s) sized to be inserted into the cavity of the steel portion,entering the copper item(s) into the steel portion through the sleeve,positioning at least one inductor in close proximity to at least parts of the outside of the steel portion,supplying electric energy to the inductor, causing induction heating of the cathode steel bar to a temperature sufficiently high and for a time sufficiently long to molten at least the outer part of the copper item(s),cooling, and solidifying the molten copper;orii) providing a steel portion of the cathode steel bar equipped with a cavity for the copper insert and a sleeve on the upper part,positioning at least one inductor in close proximity to at least parts of the outside of the steel portion,supplying electric energy to the inductor, causing induction preheating of the cathode steel bar,providing molten copper, pouring the molten copper into the cavity of the steel portion through the sleeve, cooling, and solidifying the molten copper.The method of the present invention may be a circular process where copper insert of an used cathode bar is the source of the copper insert of the cathode bar to be prepared. That is, the present invention provides a method enabling recyclability of used cathode bars with copper insert. This is advantageous in terms of flexibility, production time and cathode performance, as well as it is environmental friendly.A cathode steel bar with copper insert for use in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, obtained by the process above is also described.The present invention provides cathode bars with improved performance in terms of conductivity.In a third aspect the present invention relates to a method of removing a copper insert from an used cathode bar used in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, comprising:providing an used cathode bar,positioning an inductor in close proximity to at least parts of the cathode bar, supplying electric energy to the inductor, causing induction heating of the cathode bar to a temperature above the melting temperature of copper, forming molten copper, pouring the molten copper into a holding furnace; orcasting the molten copper into suitable items.It is also to be understood that the terminology used herein is for purpose of describing particular embodiments only, and is not intended to be limiting. It should be noted that, as used in the specification and the appended claim, the articles "a", "an", "the", and "said" are intended to mean that there are one or more of the elements unless the context explicitly dictates otherwise. Thus, for example, reference to "a unit" or "the unit" may include several devices, and the like. Furthermore, the words "comprising", "including", "containing" and similar wordings does not exclude other elements or steps. The terms “cathode bar(s)”, “cathode steel bar(s)”, “steel bar(s)”, “current collector(s)”, “cathode collector bar(s)”, “collector bar(s)” and “current collecting bar(s)”, may be used interchangeably in the present disclosure, and should be understood to denote the same entity, unless other stated.The term «copper» as used herein includes pure copper and copper alloys.The term “cavity” as used herein is to be understood as a confined space that may be open in one or more ends. A longitudinal hole in a cathode bar, open in one or both ends, is included in this term.The terms “used cathode bar(s)” and “old cathode bar(s)” or any variations of the term “cathode bar(s)” as defined above starting with the word “used” or “old”, may be used interchangeably in the present disclosure, and should be understood to denote the same entity, unless other stated.The terms “collar” and “sleeve” may be used interchangeably and has the function as feeder in the present disclosure.Brief description of drawingsFigure 1: Illustrates a cathode bar according to the invention produced by inserting a solid copper item into the steel portion.Figure 2: Illustrates a cathode bar according to the invention produced by pouring molten copper into the steel portion (top filling).Figure 3: Illustrates a cathode bar according to the invention produced by filling molten copper into the steel portion from the bottom/lower part.Figure 4: Illustrates a cathode bar according to the invention produced by filling molten copper into the steel portion from the bottom/lower part and using counter gravity casting.Figure 5: Illustrates a cathode bar according to the invention produced by filling molten copper into the steel portion from the bottom.Figure 6: Illustrates a further cathode bar according to the invention produced by filling molten copper into the steel portion from the bottom. Figure 7: Illustrates an “over the lip” filling device for filling molten in production of a cathode bar with copper insert. Figure 8: Illustrates a bottom tapping device for filling molten copper in production of a cathode bar with copper insert.Figure 9: Illustrates removing of a copper insert from an old cathode bar according to the invention.The figures 1-6 and 9 illustrates various embodiments of corresponding cathode bars. Thus, the structural parts of the cathode bars have the same reference numbers.Detailed descriptionIn the following, the present method for producing a cathode steel bar with copper insert for use in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, will be described and explained by way of examples and with reference to the accompanying drawings in which the same reference numbers refer to the same or technically equivalent elements, unless otherwise stated.Fig.1 illustrates one embodiment of the present invention, showing a cross-section of a cathode bar comprising a steel portion 2 equipped with a cavity for insertion of solid copper, and a collar or sleeve 4 of a metal material such as steel or any other suitable refractory material at the upper part acting as a feeder. The here illustrated cathode bar comprises a copper insert 1 designed as a solid rod/bar. A closing device 5 of a suitable material to prevent heat loss such as steel, titan etc., may be placed at the upper end of the cathode bar to ensure proper seal of the copper insert 1 within the steel portion 2. It should be understood that the solid copper which is the starting material of the copper insert can have several designs, e.g. a circular rod, or a rod of any geometry, or ingots or bars of any design. The only requirement of the solid copper item is that it is sized to be inserted into the cavity of the steel portion. For instance, the solid copper may be a rod with a smaller diameter than the cavity in the steel portion of the cathode bar. Another alternative is to use several copper items such as ingots and bars.In an embodiment the method comprises entering one or more solid copper item(s) 1 is/are into the steel portion 2 through the sleeve 4, and heating the steel portion 2, preferably using induction heating, until at least the outer part of the solid copper items inserted therein is molten. It may also be heated until the solid copper is fully molten. In induction heating a work-piece is heated by eddy currents induced in the work-piece. An induction heating power supply converts alternating current (AC) line power to a higher frequency AC and delivers the higher frequency AC to an inductor wherein an electromagnetic field is created within the coil of the inductor. Eddy currents will be induced in an electrically conductive work-piece placed in the electromagnetic field, generating heat in the work-piece. The inductor is commonly water cooled copper conductors made of e.g. copper tubes, profiles, plates or machined copper parts. The design of the inductor influences inter alia energy transfer to work-piece, heating rate and heating efficiency. Inductors may be helix formed or prepared from plates geometry, and the number of windings may vary. The present invention is not limited to any specific design or type of inductor. Furthermore, one or more inductors, which can be controlled separately or as a whole, may be used. For instance, the inductor may appear as being divided.At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2. Preferably, the inductor 3 is positioned such that it encircles at least partially the part of the steel portion 3 comprising the inserted copper item(s) 1. The inductor 3 is connected to a power supply (not shown in the drawings) which converts AC line power to an AC having a frequency of between 1 kHz and 50 kHz. The converted AC is delivered to the inductor 3, causing induction heating of at least a part of the steel portion 2 comprising copper item(s), encircled by the inductor 3. The steel induction heated part of the steel portion 2 is heated to a temperature above the melting temperature of copper or copper alloy. The induction heating is continued at least until the outer part of the solid copper items is molten, forming a partly or fully molten pool of copper within in the cavity of the steel portion 2.In one embodiment, the induction heating is continued after the solid copper item(s) have become molten in order to increase performance of the cathode bar. The induction heating of may be held for a period of time varying from 10 seconds to 12 hours, preferably a period of 1 minute to 1 hour.After the induction heating, the thus heated part of the steel portion 2 containing the partly or fully molten copper is cooled. Preferably, the cooling is controlled such that the lower part of the heated area is cooled first leading to solidification of the molten inner portion of copper, while the upper part is kept molten. The cooling is preferably carried out directionally such that the copper in the upper part of the steel portion is lastly solidified. Directional cooling may be obtained by upward moving of the inductor length wise along the cathode bar. Optionally, the bottom part of the steel portion 2 may be subjected to additional cooling in order to initiate the directional cooling. By such controlled cooling, piping and formation of shrink holes is reduced and controlled. A copper insert of good quality in that it is virtually pore-free and with no suctions is ensured in the cathode bar.Fig.2 illustrates another embodiment of the present invention, showing a cross-section of a cathode bar comprising a steel portion 2 equipped with a cavity for filling of molten copper 6, and a collar or sleeve of a metal material such as steel or any other suitable refractory material at the upper part acting as a feeder.In this embodiment, the method comprises preheating of the steel portion 2 of the cathode by residual heat from previously heated cathode bars and/or by utilizing induction heating.At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2. The properties and design of the inductor to be used in this embodiment correspond to the aforementioned description of inductor.Preferably, the inductor 3 is positioned such that it encircles at least partially the part of the steel portion 3 comprising the cavity for filling molten copper. The inductor 3 is connected to a power supply (not shown in the drawings) which converts AC line power to an AC having a frequency of between 1 kHz and 50 kHz. The converted AC is delivered to the inductor 3, causing induction heating of at least a part of the steel portion 2 encircled by the inductor 3. The steel induction heated part of the steel portion 2 is heated to a temperature above the melting temperature of copper or copper alloy. Molten copper is provided, e.g. from used cathode bars or any other source, and filled into the steel portion 2 of the cathode bar, either filling from top or bottom with a suitable casting method.In one embodiment, the induction heating of the steel portion 2 is continued after filling of molten copper into the cavity of the steel portion 2 in order to increase performance of the cathode bar. The induction heating of may be held for a period of time varying from 10 seconds to 12 hours, preferably a period of 1 minute to 1 hour. After the induction heating, the thus heated part of the steel portion 2 containing the partly or fully molten copper is cooled. Preferably, the cooling is controlled such that the lower part of the heated area is cooled first leading to solidification of the molten inner portion of copper, while the upper part is kept molten. The cooling is preferably carried out directionally such that the copper in the upper part of the steel portion is lastly solidified. Directional cooling may be obtained upward moving of the inductor length wise along the cathode bar. Optionally, the bottom part of the steel portion 2 may be subjected to additional cooling in order to initiate the directional cooling. By such controlled cooling, piping and formation of shrink holes is reduced and controlled. A copper insert of good quality in that it is virtually pore-free and with no suctions is ensured in the cathode bar.Fig.3 illustrates further embodiment of the present invention where molten copper is filled into the steel portion from the bottom or through an opening in the steel portion 2 placed anywhere along its side below the sleeve 4 at the top, i.e. through a permanent steel mold with gating. Fig.3 is showing a cross-section of a cathode bar comprising said a permanent steel mold with gating/a steel portion 2 equipped with a cavity for filling of molten copper, and a collar or sleeve 4 of a metal material such as steel or any other suitable refractory material at the upper part. A downsprue 7 for filling of molten copper is connected to the steel portion 2 so that the molten copper is filled into the cavity of the steel portion. The connection point is shown at the lower part of the steel portion, but may be anywhere along the side of the steel portion 2. Only one steel portion 2 is shown, but typically a number of steel portions 2/ permanent steel molds with gating are connected to the downsprue 7 for simultaneous filling of molten copper. At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2 in a similar way as explained with regard to Fig.2 above. Molten copper is filled at a desired level in the cavity of the steel portion 2 and the sleeve 4 acts as a prolongation of the cavity to protect against overfilling and will secure good quality copper. The collar/sleeve 4 may also be a designed as a separate part connected to the steel portion 2. Heating and cooling are performed as discussed for the embodiment of Fig.2. The inductor 3 will direct the solidification towards the collar/sleeve 4. During cooling the copper level decreases. Solidified copper on the edge of the sleeve 4 may be removed by means of drilling, machining or any other suitable method, and a closing device 5 (not shown) may be introduced. During filling of the molten copper, the steel portion 2 of the cathode bar is preferably kept at an angle to reduce pressure height and to improve the filling process by avoiding turbulence and/or oxide formation. After the filling the steel portion 2 with molten copper, the steel portion 2 may be tilted to a vertical position or any other position. This embodiment is illustrated in Fig.4 showing a cathode bar according to the invention produced by filling molten copper 6 into the steel portion 2 at the lower end and equipped with an inductor 3, by using counter gravity casting.Fig.5 illustrates further embodiment of the present invention where molten copper is filled into the steel portion from the bottom of the steel portion 2. Fig.5 is showing a cross-section of a cathode bar comprising said a steel portion 2 equipped with a cavity for filling of molten copper, and a collar or sleeve 4 of a metal material such as steel or any other suitable refractory material at the upper part. A downsprue 7 for filling of molten copper is connected to the steel portion 2 so that the molten copper is filled into the cavity of the steel portion from its bottom/underside. Only one steel portion 2 is shown, but typically a number of steel portions 2 are connected to the downsprue 7 for simultaneous filling of molten copper. At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2 in a similar way as explained with regard to Fig.2 above. Molten copper is filled at a desired level in the cavity of the steel portion 2 and the sleeve 4 acts as a protection against overfilling and will secure good quality copper. The sleeve 4 shown in Fig.5 is placed at the top of the steel portion 2, but any location further down on the side of the steel portion 2 is within the scope of the invention. Heating and cooling are performed as discussed for the embodiment of Fig.2. The inductor 3 directs the solidification towards the sleeve 4. During cooling the copper level decreases. Solidified copper on the edge of the sleeve 4 may be removed by means of drilling, machining or any other suitable method, and a closing device 5 (not shown) may be introduced.Fig.6 illustrates still a further embodiment of the present invention where molten copper is filled into the steel portion from the bottom of the steel portion 2. Fig.6 is showing a cross-section of a cathode bar comprising said a steel portion 2 equipped with a cavity for filling of molten copper, and a collar or sleeve 4 of a metal material such as steel or any other suitable refractory material at the upper part. A reservoir of molten copper equipped with a feeder P for addition of molten copper to the reservoir and a supply pipe 8 connected to the steel portion 2, is arranged below the steel portion 2. Molten copper is filled into the cavity of the steel portion from its bottom/underside through the supply pipe 8. At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2 in a similar way as explained with regard to Fig.2 above. Molten copper is filled at a desired level in the cavity of the steel portion 2 and the sleeve 4 acts as a protection against overfilling and secure good quality copper. The sleeve 4 shown in Fig.6 is placed at the upper part of the steel portion 2, but may be located further down on the side of the steel portion. Heating and cooling are performed as discussed for the embodiment of Fig.2. The inductor 3 directs the solidification towards the sleeve 4. During cooling the copper level decreases. Solidified copper on the edge of the sleeve 4 may be removed by means of drilling, machining or any other suitable method, and a closing device 5 (not shown) may be introduced.Fig.7 illustrates an “over the lip” filling device and Fig.8 a bottom tapping device for filling molten copper in production of a cathode bar with copper insert. Both devices are commercial available and within the knowledge of the skilled person. “Over the lip” filling and bottom tapping are useful filling methods for carrying out the embodiments of the invention related to filling molten copper when producing the cathode bars with copper insert such as illustrated in Figs.2-6.Fig.9 illustrates removing of a copper insert 1 from a used cathode bar. A cross-section of a cathode bar comprising a steel portion 2 and a copper insert 1 is shown illustrating the embodiment of the present invention where copper is melted out for optional re-use in production of a new cathode steel bar as described in the embodiment above.In this embodiment, a used cathode steel bar is provided and prepared for copper melt out, typically through a cutting process or similar to gain direct access to the copper insert of the cathode bar.The cathode bar is preferably preheated by rest heat from previously heated cathode bars and subsequently heated by utilizing induction heating to at least the melting point of copper or copper alloy.At least one inductor 3 is positioned in close proximity to at least parts of the outside of the steel portion 2. The properties and design of the inductor to be used in this embodiment correspond to the aforementioned description of inductor. Preferably, the inductor 3 is positioned such that it encircles at least partially the part of the cathode bar comprising the copper insert. The inductor 3 is connected to a power supply as described above and causes induction heating of at least a part of the cathode bar encircled by the inductor 3. When reaching the melting point of the copper, molten copper is formed and poured out of the steel portion 2 of the cathode bar into a holding furnace, or casted directly into copper ingots or similar solid copper items.In the embodiment where molten copper is poured into a holding furnace, it may be reused directly in molten state for production of new cathode bars as described above in relation to Figs.2-8.In the embodiment where the copper is casted into solid copper items, they may be reused for production of new cathode bars as described above in relation to Fig.1, or Figs.2-6 by re-melting of the solid copper items.Refining or “dilution” of the recycled copper to desired quality might be required. Here “dilution” means addition of more pure copper.Having described preferred embodiments of the invention it will be apparent to those skilled in the art that other embodiments incorporating the concepts may be used. These and other examples of the invention illustrated above are intended by way of example only and the actual scope of the invention is to be determined from the claims.
Claims
P a t e n t c l a i m s1. A method for producing a cathode steel bar with copper insert for use in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, c h a r a c t e r i s e d i n t h a t it comprises:i) providing a steel portion of the cathode steel bar equipped with a cavity for the copper insert and a sleeve on the upper part,providing one or more solid copper item(s) sized to be inserted into the cavity of the steel portion,entering the copper item(s) into the steel portion through the sleeve, positioning at least one inductor in close proximity to at least parts of the outside of the steel portion,supplying electric energy to the inductor, causing induction heating of the cathode steel bar to a temperature sufficiently high and for a time sufficiently long to molten at least the outer part of the copper item(s),cooling, and solidifying the molten copper;orii) providing a steel portion of the cathode steel bar equipped with a cavity for the copper insert and a sleeve on the upper part,positioning at least one inductor in close proximity to at least parts of the outside of the steel portion,supplying electric energy to the inductor, causing induction preheating of the cathode steel bar,providing molten copper,pouring the molten copper into the cavity of the steel portion through the sleeve, cooling, and solidifying the molten copper.2. The method, according to claim 1, comprising supplying electric energy with a frequency of between 1 kHz to 50 kHz from a power unit to the inductor.3. The method, according to any one of the previous claims 1-2, wherein the heating and preheating temperature is above the melting temperature of copper or copper alloy.4. The method, according to any one of the previous claims 1-3, wherein the heating and preheating be held for a period of 10 seconds to 12 hours, preferably a period of 1 minute to 1 hour.5. The method, according to any one of the previous claims 1-4, wherein the cooling is carried out directionally, in a direction from the lower part of the cathode bar towards its upper part.6. The method, according to claims 5, wherein the directional cooling is obtained by upward moving of the inductor length wise along the cathode bar.7. The method, according to any one of the previous claims 1-6, wherein the method is circular in that the solid copper item(s) or molten copper is provided from used cathode bars.8. The method, according to any one of the previous claims 1-7, wherein the solid copper item(s) is provided from used cathode bars.9. The method, according to any one of the previous claims 1-6, wherein pouring of the molten copper into the cavity of the steel portion is obtained by top filling.10. The method, according to any one of the previous claims 1-6, wherein filling of the molten copper into the cavity of the steel portion is carried out by top or bottom filling.11. The method, according to any one of the previous claims 9-10, wherein the steel portion of the copper bar is kept at an angle during filling of molten copper.12. The method, according to any one of the previous claims 1-6 and 9-11, wherein the molten copper is provided from used cathode bars.13. A method of removing a copper insert from a cathode bar used in an electrolytic cell for the electrolytic production of aluminium using the Hall-Héroult process, c h a r a c t e r i s e d i n t h a t it comprises:- providing an used cathode bar,- positioning an inductor in close proximity to at least parts of the cathode bar, - supplying electric energy to the inductor, causing induction heating of the cathode bar to a temperature above the melting temperature of copper, forming molten copper,- pouring the molten copper into a holding furnace; or- casting the molten copper into suitable items.14. The method, according to claim 13, comprising supplying electric energy with a frequency of between 1 kHz to 50 kHz from a power unit to the inductor.Patentkrav1. Fremgangsmåte for fremstilling av en katodestålskinne med kobberinnsats for anvendelse i en elektrolytisk celle for elektrolytisk fremstilling av aluminium ved bruk av Hall-Héroult-prosessen, k a r a k t e r i s e r t v e d a t den omfatter:i) å tilveiebringe en ståldel av katodestålskinnen utstyrt med et hulrom for kobberinnsatsen og en hylse på den øvre del,tilveiebringe ett eller flere faste kobberelement(er) dimensjonert for å settes inn i hulrommet på ståldelen,innføre kobberelement(ene) i ståldelen gjennom hylsen,plassere minst én induktor i umiddelbar nærhet til i det minste deler av utsiden av ståldelen,tilføre elektrisk energi til induktoren, som forårsaker induksjonsoppvarming av katodestålskinnen til en temperatur som er tilstrekkelig høy og i en periode som er tilstrekkelig lang til å smelte i det minste den ytre delen av kobberelementet(ene), kjøle og størkne det smeltede kobber;ellerii) å tilveiebringe en ståldel av katodestålskinnen utstyrt med et hulrom for kobberinnsatsen og en hylse på den øvre del,plassere minst én induktor i umiddelbar nærhet til i det minste deler av utsiden av ståldelen,tilføre elektrisk energi til induktoren, som forårsaker induksjonsforvarming av katodestålskinnen,tilveiebringe smeltet kobber,helle det smeltede kobber inn i hulrommet i ståldelen gjennom hylsen, kjøle og størkne det smeltede kobber.2. Fremgangsmåte ifølge krav 1, omfattende å tilføre elektrisk energi med en frekvens på mellom 1 kHz til 50 kHz fra en kraftenhet til induktoren.3. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-2, der oppvarmings- og forvarmingstemperaturen er over smeltetemperaturen for kobber eller kobberlegering.4. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-3, der oppvarmingen og forvarmingen holdes i en periode på 10 sekunder til 12 timer, fortrinnsvis en periode på 1 minutt til 1 time.5. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-4, der kjølingen utføres retningsbestemt, i en retning fra den nedre del av katodeskinnen mot den øvre del.6. Fremgangsmåte ifølge krav 5, der den retningsbestemte kjølingen oppnås ved å bevege induktoren oppover langs lengden av katodeskinnen.7. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-6, der fremgangsmåten er sirkulær ved at det eller de faste kobberelement(ene) eller smeltet kobber tilveiebringes fra brukte katodeskinner.8. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-7, der det/de faste kobberelement(ene) tilveiebringes fra brukte katodeskinner.9. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-6, der hellingen av det smeltede kobber inn i hulrommet i ståldelen oppnås ved toppfylling.10. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-6, der fylling av det smeltede kobber inn i hulrommet på ståldelen utføres ved topp- eller bunnfylling.11. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 9-10, der ståldelen av kobberskinnen holdes i en vinkel under fylling av smeltet kobber.12. Fremgangsmåte ifølge et hvilket som helst av de foregående kravene 1-6 og 9-11, der det smeltede kobber tilveiebringes fra brukte katodeskinner.13. Fremgangsmåte for å fjerne en kobberinnsats fra en katodeskinne anvendt i en elektrolytisk celle for elektrolytisk fremstilling av aluminium ved bruk av Hall-Héroultprosessen, k a r a k t e r i s e r t v e d a t den omfatter:- å tilveiebringe en brukt katodeskinne,- plassere en induktor i umiddelbar nærhet til i det minste deler av katodeskinnen, - tilføre elektrisk energi til induktoren, som forårsaker induksjonsoppvarming av katodeskinnen til en temperatur over smeltetemperaturen for kobber, danne smeltet kobber,- helle det smeltede kobber inn i en holdeovn; eller- støpe det smeltede kobber i passende elementer.14. Fremgangsmåte ifølge krav 13, omfattende å tilføre elektrisk energi med en frekvens på mellom 1 kHz til 50 kHz fra en kraftenhet til induktoren.
Drawings

Priority

No priority

Patent classes

IPC classesC25C 3/16C25C 3/08CPC classesC25C 3/16C25C 3/08

Citations

CN 210237797 U (U)US 4347661 A (A)CN 206457546 U (U)WO 0242525 A1 (A1)US 2005218006 A1 (A1)

Applicants, owners and inventors

Owners
STORVIK AS
Industrivegen 13 6600 SUNNDALSØRA NO (SUNNDAL Municipality, Møre og Romsdal county)Org. number: 992027576Inventors
Bjarte Valåmo
Nordfallet 40 8646 KORGEN NO (HEMNES Municipality, Nordland county)
Eirik Belland
Kursetvegen 6 6019 ÅLESUND NO (Ã…LESUND Municipality, Møre og Romsdal county)

Agent

ZACCO NORWAY AS
ZACCO NORWAY AS

Org. number: 982702887

Name and address are automatically synchronized with the Brønnøysund Register Centre.

Open in The Brønnøysund Register Centre
Postboks 488 0213 OSLO NO (OSLO Municipality, Oslo county)
Org. number: 982702887
Reference: P342103NO00

Status history

Payment history

Oppositions and appeals

No oppositions or appeals

Administrative limitation

No administrative limitation

Liens and licences

No liens or licenses registered

Gazette entries

No Gazette entries foundOnly events from 2024.03.04 and onwards are shown.